(Summary description)The hazard of cavitation corrosion of the cylinder steel pipe is quite large, it will cause the mating surface to become black, and even the support ring and sealing ring will be burnt, which will cau

What are the main causes of cavitation in the cylinder tube?

(Summary description)The hazard of cavitation corrosion of the cylinder steel pipe is quite large, it will cause the mating surface to become black, and even the support ring and sealing ring will be burnt, which will cau

  • Categories:Steel knowledge
  • Author:
  • Origin:
  • Time of issue:2020-10-10 10:11
  • Views:
Information

The hazard of cavitation corrosion of the cylinder steel pipe is quite large, it will cause the mating surface to become black, and even the support ring and sealing ring will be burnt, which will cause internal leakage of the hydraulic cylinder. When cavitation is common with other types of corrosion When used, it will accelerate the corrosion rate of the main parts of the cylinder steel pipe several times or even dozens of times, which will seriously affect the normal use of construction machinery. Therefore, it is very necessary to prevent the cavitation of the hydraulic cylinder barrel.

⑴ Essential analysis of cavitation

       Cavitation occurs mainly because a certain amount of air is mixed into the oil between the piston and the guide sleeve during the working process of the hydraulic cylinder. As the pressure gradually increases, the gas in the oil will become air bubbles When the pressure rises to a certain limit value, these bubbles will burst under the action of high pressure, which will quickly act on the surface of the part with high temperature and high pressure, causing the hydraulic cylinder to produce cavitation and causing the parts to fail. Corrosive damage.

⑵Unqualified hydraulic oil quality leads to cavitation

       Ensuring the quality of hydraulic oil is an important factor in preventing cavitation. If the oil has poor anti-foaming properties, it is easy to produce foam, which will lead to cavitation. Secondly, the frequency of oil pressure changes is too fast and too high. , It will also directly cause the formation of bubbles and accelerate the bursting speed of bubbles. Tests have proved that the speed of cavitation in the parts with high frequency of pressure changes will increase. For example, the hydraulic cylinder inlet and return ports, etc., due to the frequency of pressure changes Relatively high, the degree of cavitation is relatively higher than other parts. In addition, overheating of the oil will also increase the probability of cavitation.

⑶Improper manufacturing and maintenance lead to cavitation

       Because the hydraulic system is not fully exhausted during assembly or maintenance, there is gas in the system, which can cause cavitation under the action of high temperature and high pressure.

⑷The quality of coolant causes cavitation

       When the coolant contains corrosive media, such as various acid radical ions, oxidants, etc., it is prone to chemical and electrochemical corrosion. Under their combined action, the speed of cavitation will also be accelerated; if the cooling system is well maintained, it can be Prevent the occurrence of cavitation. For example, if the pressure cover of the radiator of the cooling system is well maintained, the pressure of the radiator's coolant can always be higher than the vapor pressure, thereby preventing the occurrence of cavitation. Another example is the section of the cooling system. Thermostat; a thermostat with good performance can keep the coolant in a suitable temperature range and reduce the energy released when the bubble bursts.

Scan the QR code to read on your phone

Recommended Products

JIS G3445 STKM11A/12A/13A COLD ROLLED PRECISION STEEL TUBE
Mechanical tube 标准 Standard: JIS G3445   用途 Application: 适用于机械制造,汽车制造,自行车制造,家具制作以及其他机械的零部件制造。 It is widely used in manufacturing of Machinery, Automobile, bycycle, furniture and some other machined parts. 主要牌号 Steel Tube Grade:   STKM 11A, STKM12(A,BC),STKM13(A,B,C),STKM14(A,B,C)   化学成分 Chemical Composition   钢级 Standard 牌号 Grade 化学成分Chemical Composition C Si Mn P S JIS G3445 STKM11A ≤0.12 ≤0.35 ≤0.60 ≤0.040 ≤0.040 STKM12A ≤0.20 ≤0.35 ≤0.60 ≤0.040 ≤0.040 STKM12B STKM12C STKM13A ≤0.25 ≤0.35 0.30-0.90 ≤0.040 ≤0.040 STKM13B STKM13C STKM14A ≤0.30 ≤0.35 0.30-1.00 ≤0.040 ≤0.040 STKM14B STKM14C   机械性能 Mechanical Properties   钢级 Standard 牌号 Grade 机械性能Mechanical Properties 抗拉强度(Mpa) 屈服强度(Mpa) 伸长率(%) Tensile Strength Yield Strength Elongation JIS G3445 STKM11A ≥295 / ≥35 STKM12A ≥345 ≥175 ≥35 STKM12B ≥390 ≥275 ≥35 STKM12C ≥470 ≥355 ≥25 STKM13A ≥375 ≥215 ≥30 STKM13B ≥440 ≥305 ≥20 STKM13C ≥510 ≥380 ≥15 STKM14A ≥410 ≥245 ≥25 STKM14B ≥500 ≥355 ≥15 STKM14C ≥550 ≥410 ≥15  
More 白箭头 黑箭头
42CrMo4 precision seamless steel tube for auto parts
42CrMo4 precision seamless steel tube for auto parts   chemical composition:   Carbon C  0.38~0.45% Silicon Si  0.17~0.37% Manganese Mn  0.50~0.80% Sulfur S  Allow residual content ≤0.035% Phosphorus P  allowable residual content ≤0.035% Chromium Cr  0.90~1.20% Nickel Ni  allowable residual content ≤0.30% Copper Cu  allowable residual content ≤0.30% Mo  0.15~0.25%     Mechanical properties: Hardness: Annealing, 255~207HB, indentation diameter 3.8~4.2mm; Quenching, ≥60HRC cr12mov The hardenability, hardness, strength and toughness after quenching and tempering are higher than CR12, and the work with a diameter of 300-400mm or less can be completed Hardenable, small quenching deformation, but poor high temperature plasticity. cr12mov plates are mostly used to manufacture composite molds and tools with large cross-sections, complex shapes and heavy workloads.  
More 白箭头 黑箭头
Mild Steel TUBE STKM11A /STKM13 A
Mechanical tube Standard: JIS G3445 Application: It is widely used in manufacturing of Machinery, Automobile, bycycle, furniture and some other machined parts. Steel Tube Grade: STKM 11A, STKM12(A,BC),STKM13(A,B,C),STKM14(A,B,C) Chemical Composition
More 白箭头 黑箭头
GB/T8162/8163 HOT ROLLED SEAMLESS STEEL PIPE
GB/T8162/8163 HOT ROLLED SEAMLESS STEEL PIPE
More 白箭头 黑箭头

There is currently no information to display
Please add data record on website background.

Shandong Liaocheng Yuanhetai Steel Co., Ltd. |   鲁ICP备20028590号-1  |  Powered by www.300.cn