The latest process of cold drawn quilted pipe

The latest process of cold drawn quilted pipe

  • Categories:Industry News
  • Author:
  • Origin:
  • Time of issue:2020-10-10 10:09
  • Views:

(Summary description)Cold drawn (rolled) seamless steel pipe: round tube billet → heating → piercing → heading → annealing → pickling → oiling (copper plating) → multi-pass cold drawing (cold rolling) → billet tube → heat

The latest process of cold drawn quilted pipe

(Summary description)Cold drawn (rolled) seamless steel pipe: round tube billet → heating → piercing → heading → annealing → pickling → oiling (copper plating) → multi-pass cold drawing (cold rolling) → billet tube → heat

  • Categories:Industry News
  • Author:
  • Origin:
  • Time of issue:2020-10-10 10:09
  • Views:
Information

Cold drawn (rolled) seamless steel pipe: round tube billet → heating → piercing → heading → annealing → pickling → oiling (copper plating) → multi-pass cold drawing (cold rolling) → billet tube → heat treatment → straightening → Hydraulic test (flaw detection) → mark → warehousing.

    What is a cold drawn quilted tube? Hot-rolled steel pipes use continuous casting slabs or blooming slabs as raw materials, which are heated by a walking heating furnace, and then enter the roughing mill after high-pressure water descaling. The rough-rolled materials are cut head, tail, and then enter the finishing mill for computer control After rolling, after the final rolling, it is cooled by laminar flow and coiled by a coiler to become a straight hair coil. The head and tail of straight hair curlers are often tongue-shaped and fish-tail-shaped, with poor thickness and width accuracy, and the edges often have defects such as wave shape, hemming, and tower shape.

    The coil weight is heavier and the inner diameter of the steel coil is 760mm. (Generally used in the pipe making industry.) After the straight hair coil is processed by the head, tail, trim and multi-pass straightening, leveling and other finishing lines, then it is cut or recoiled to become: hot rolling Steel plates, flat hot-rolled steel coils, slitting strips and other products. If the hot-rolled finished coil is pickled to remove the oxide scale and coated with oil, it becomes a hot-rolled pickled coil. This product has a tendency to partially replace cold-rolled plates, and the price of seamless steel pipes is moderate, which is very popular among users.

     Cold-drawn steel pipes use hot-rolled steel coils as raw materials. After pickling to remove the oxide scale, they are cold-rolled. The finished products are hard-rolled coils. The cold-work hardening caused by continuous cold deformation increases the strength, hardness and toughness of the hard-rolled coils. The plastic index drops, so the stamping performance will deteriorate, and it can only be used for simple deformed parts. Hard-rolled coils can be used as raw materials for hot-dip galvanizing plants because all hot-dip galvanizing units are equipped with annealing lines. The weight of the rolled hard coil is generally 6 to 13.5 tons, and the inner diameter of the steel coil is 610mm.

    Generally, cold continuous rolled plates and coils should undergo continuous annealing (CAPL unit) or bell furnace annealing to eliminate cold work hardening and rolling stress, and meet the mechanical performance indicators specified by the corresponding standards.
    The surface quality, appearance, and dimensional accuracy of cold-rolled steel sheets are better than those of hot-rolled steel sheets, and the thickness of their products is as thin as about 0.18mm, so they are favored by users. The cold-rolled steel coil is used as the base plate for deep processing of the product, which becomes a high value-added product.

    Such as electro-galvanized, hot-dip galvanized, fingerprint-resistant electro-galvanized, color-coated steel coil and vibration-damping composite steel plate, PVC composite steel plate, etc., which make these products have excellent qualities such as beautiful appearance and high corrosion resistance, and have been widely used. The cold-rolled steel coil must be finished after annealing, including cutting head, tail, trimming, leveling, leveling, recoiling, or longitudinal shearing. Cold rolled products are widely used in industries such as automobile manufacturing, household appliances, instrument switches, construction, and office furniture. The weight of each bale after the steel plate is bundled is 3 to 5 tons. The flat sub-roll weight is generally 3~10 tons/roll. The inner diameter of the coil is 610mm.

Scan the QR code to read on your phone

Recommended Products

JIS G3445 STKM11A/12A/13A COLD ROLLED PRECISION STEEL TUBE
Mechanical tube 标准 Standard: JIS G3445   用途 Application: 适用于机械制造,汽车制造,自行车制造,家具制作以及其他机械的零部件制造。 It is widely used in manufacturing of Machinery, Automobile, bycycle, furniture and some other machined parts. 主要牌号 Steel Tube Grade:   STKM 11A, STKM12(A,BC),STKM13(A,B,C),STKM14(A,B,C)   化学成分 Chemical Composition   钢级 Standard 牌号 Grade 化学成分Chemical Composition C Si Mn P S JIS G3445 STKM11A ≤0.12 ≤0.35 ≤0.60 ≤0.040 ≤0.040 STKM12A ≤0.20 ≤0.35 ≤0.60 ≤0.040 ≤0.040 STKM12B STKM12C STKM13A ≤0.25 ≤0.35 0.30-0.90 ≤0.040 ≤0.040 STKM13B STKM13C STKM14A ≤0.30 ≤0.35 0.30-1.00 ≤0.040 ≤0.040 STKM14B STKM14C   机械性能 Mechanical Properties   钢级 Standard 牌号 Grade 机械性能Mechanical Properties 抗拉强度(Mpa) 屈服强度(Mpa) 伸长率(%) Tensile Strength Yield Strength Elongation JIS G3445 STKM11A ≥295 / ≥35 STKM12A ≥345 ≥175 ≥35 STKM12B ≥390 ≥275 ≥35 STKM12C ≥470 ≥355 ≥25 STKM13A ≥375 ≥215 ≥30 STKM13B ≥440 ≥305 ≥20 STKM13C ≥510 ≥380 ≥15 STKM14A ≥410 ≥245 ≥25 STKM14B ≥500 ≥355 ≥15 STKM14C ≥550 ≥410 ≥15  
More 白箭头 黑箭头
42CrMo4 precision seamless steel tube for auto parts
42CrMo4 precision seamless steel tube for auto parts   chemical composition:   Carbon C  0.38~0.45% Silicon Si  0.17~0.37% Manganese Mn  0.50~0.80% Sulfur S  Allow residual content ≤0.035% Phosphorus P  allowable residual content ≤0.035% Chromium Cr  0.90~1.20% Nickel Ni  allowable residual content ≤0.30% Copper Cu  allowable residual content ≤0.30% Mo  0.15~0.25%     Mechanical properties: Hardness: Annealing, 255~207HB, indentation diameter 3.8~4.2mm; Quenching, ≥60HRC cr12mov The hardenability, hardness, strength and toughness after quenching and tempering are higher than CR12, and the work with a diameter of 300-400mm or less can be completed Hardenable, small quenching deformation, but poor high temperature plasticity. cr12mov plates are mostly used to manufacture composite molds and tools with large cross-sections, complex shapes and heavy workloads.  
More 白箭头 黑箭头
Mild Steel TUBE STKM11A /STKM13 A
Mechanical tube Standard: JIS G3445 Application: It is widely used in manufacturing of Machinery, Automobile, bycycle, furniture and some other machined parts. Steel Tube Grade: STKM 11A, STKM12(A,BC),STKM13(A,B,C),STKM14(A,B,C) Chemical Composition
More 白箭头 黑箭头
GB/T8162/8163 HOT ROLLED SEAMLESS STEEL PIPE
GB/T8162/8163 HOT ROLLED SEAMLESS STEEL PIPE
More 白箭头 黑箭头

There is currently no information to display
Please add data record on website background.

Shandong Liaocheng Yuanhetai Steel Co., Ltd. |   鲁ICP备20028590号-1  |  Powered by www.300.cn